| Line 31: | Line 31: | ||
|- | |- | ||
| 01/05/2016 || LY scan || At 100ns, as described in run 3047. | | 01/05/2016 || LY scan || At 100ns, as described in run 3047. | ||
| + | |- | ||
| + | | 03/04/2016 || Transverse Transmittance || At the center of the crystal, every nm from 200nm until 800nm. Sample: 1315 | ||
| + | |- | ||
| + | | 03/04/2016 || Dimensions || Crystal's dimensions measured. Length and six points of width (3 in each face). | ||
|} | |} | ||
Revision as of 16:27, 4 March 2016
| ⇐ Back to Crystal LOG |
| ⇐ Back to Neutral Particle Spectrometer |
| ⇐ Back to the Main_Page |
Time LOG
| Date | Description | Comments |
|---|---|---|
| 12/14/2015 | Pictures | Documentation of crystal's conditions as it arrived at CUA. |
| 12/15/2015 | Thermal annealing | Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. |
| 12/17/2015 | Long. Transmittance | Note: crystal NOT wrapped. |
| 12/17/2015 | Transverse Transmittance | Scan at 360, 420, and 620nm. |
| 12/18/2015 | Irradiation | 160 keV photons at 6mA, for 10min. |
| 12/18/2015 | Transverse Transmittance | Scan at 360, 420, and 620nm after 30 min of irradiation. |
| 01/05/2016 | LY scan | At 100ns, as described in run 3047. |
| 03/04/2016 | Transverse Transmittance | At the center of the crystal, every nm from 200nm until 800nm. Sample: 1315 |
| 03/04/2016 | Dimensions | Crystal's dimensions measured. Length and six points of width (3 in each face). |