Difference between revisions of "MainPage:Nuclear:NPS:PWO:CrystalLOG:SICCAJ35"
Jump to navigation
Jump to search
| Line 21: | Line 21: | ||
|- | |- | ||
| 03/18/2016 || Thermal annealing || Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. | | 03/18/2016 || Thermal annealing || Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. | ||
| + | |- | ||
| + | | 04/24/2016 || Light Yield || Run 3196: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. LY = **** pe/MeV. | ||
|} | |} | ||
Revision as of 19:57, 24 April 2016
| ⇐ Back to Crystal LOG |
| ⇐ Back to Neutral Particle Spectrometer |
| ⇐ Back to the Main_Page |
Time LOG
| Date | Description | Comments |
|---|---|---|
| 03/17/2016 | Pictures | Documentation of crystal's conditions as it arrived at CUA. |
| 03/18/2016 | Thermal annealing | Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. |
| 04/24/2016 | Light Yield | Run 3196: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. LY = **** pe/MeV. |