| Line 30: | Line 30: | ||
| 05/23/2016 || Transverse Transmittance Scan || Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. | | 05/23/2016 || Transverse Transmittance Scan || Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. | ||
|- | |- | ||
| − | | 07/06/2016 || Longitudinal Transmittance Scan || Wavelengths: 200-800nm | + | | 07/06/2016 || Longitudinal Transmittance Scan || Wavelengths: 200-800nm. |
|- | |- | ||
| − | | 07/18/2016 || Transverse Transmittance Scan || Wavelengths: 200-800nm | + | | 07/18/2016 || Transverse Transmittance Scan || Wavelengths: 200-800nm. |
|- | |- | ||
| − | | 07/21/2016 || Xray Radiation || 70 minutes, 160mV, 6mA. | + | | 07/21/2016 || Xray Radiation || 70 minutes, 160mV, 6mA. ? mm from beam origin. |
|- | |- | ||
| 07/21/2016 || Transverse Transmittance Scan || Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. | | 07/21/2016 || Transverse Transmittance Scan || Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. | ||
| + | |- | ||
| + | | 07/27/16 || X-Ray Radiation || 160mV, 6.3 mA, 99 minutes. | ||
| + | |- | ||
| + | | 07/27/16 || Transverse Transmission || Wavelengths: 200-800nm. | ||
| + | |- | ||
| + | | 07/27/2016 || LED curing || 3.0 V for 7 minutes. | ||
| + | |- | ||
| + | | 07/27/2016 ||Transverse Transmittance || Wavelengths: 200-800nm. | ||
|} | |} | ||
Revision as of 14:20, 27 July 2016
| ⇐ Back to Crystal LOG |
| ⇐ Back to Neutral Particle Spectrometer |
| ⇐ Back to the Main_Page |
Time LOG
| Date | Description | Comments |
|---|---|---|
| 12/14/2015 | Pictures | Documentation of crystal's conditions as it arrived at CUA. |
| 01/28/2016 | Thermal annealing | Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. |
| 03/03/2016 | Light Yield | Run 3149: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. LY = 13.07 pe/MeV. |
| 03/04/2016 | Transverse Transmittance | At the center of the crystal, every nm from 200nm until 800nm. Sample: 1308 |
| 03/04/2016 | Dimensions | Crystal's dimensions measured. Length and six points of width (3 in each face). |
| 05/23/2016 | Transverse Transmittance Scan | Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/06/2016 | Longitudinal Transmittance Scan | Wavelengths: 200-800nm. |
| 07/18/2016 | Transverse Transmittance Scan | Wavelengths: 200-800nm. |
| 07/21/2016 | Xray Radiation | 70 minutes, 160mV, 6mA. ? mm from beam origin. |
| 07/21/2016 | Transverse Transmittance Scan | Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/27/16 | X-Ray Radiation | 160mV, 6.3 mA, 99 minutes. |
| 07/27/16 | Transverse Transmission | Wavelengths: 200-800nm. |
| 07/27/2016 | LED curing | 3.0 V for 7 minutes. |
| 07/27/2016 | Transverse Transmittance | Wavelengths: 200-800nm. |