**SICCA J26**
Date	Description	Comments
03/09/2016	Pictures	Documentation of crystal's conditions as it arrived at CUA.
03/09/2016	Dimensions	Crystal's dimensions measured. Length and six points of width (3 in each face).
03/18/2016	Thermal annealing	Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour.
03/30/2016	Light Yield	Run 3166: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. LY = 10.87 pe/MeV.
05/19/2016	Transverse Transmittance	At the center of the crystal, every nm from 200nm until 800nm. Sample: 1345
05/20/2016	Transverse Transmittance Scan	Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s.
07/06/2016	Longitudinal Transmittance Scan	Wavelengths: 200-800nm. Sampling period: 0.6s, moving motor at 2mm/s.
07/21/2016	Light Yield	Run:3236 ~3layers of teflon tape and 1 layer of black tape. ~50,000 incidents recorded at ~18 degrees Celsius.
07/27/2016	X-ray Irradiation	160 mV, 6.3 mA, 99 minutes.
07/27/2016	Transverse Transmittance	Wavelengths: 200-800nm.
07/27/2016	LED curing	3.0V for 7 minutes.
07/27/2016	Transverse Transmittance	Wavelenths: 200-800nm.

@@ Line 33: / Line 33: @@
 |-
 | 07/21/2016 || Light Yield || Run:3236 ~3layers of teflon tape and 1 layer of black tape. ~50,000 incidents recorded at ~18 degrees Celsius.
+|-
+| 07/27/2016 || X-ray Irradiation || 160 mV, 6.3 mA, 99 minutes.
+|-
+| 07/27/2016 || Transverse Transmittance || Wavelengths: 200-800nm.
+|-
+| 07/27/2016 || LED curing || 3.0V for 7 minutes.
+|-
+| 07/27/2016 || Transverse Transmittance || Wavelenths: 200-800nm.
 |}