Difference between revisions of "MainPage:Nuclear:NPS:PWO:CrystalLOG:SICCAJ22"
Jump to navigation
Jump to search
| Line 47: | Line 47: | ||
| valign="top"| | | valign="top"| | ||
[[File:SICCAJ22.JPG|thumb|center|340px|xxxx.]] | [[File:SICCAJ22.JPG|thumb|center|340px|xxxx.]] | ||
| + | |||
| + | ==Radiation Hardness== | ||
| + | {|border="0" style="text-align:center;" width="100%" | ||
| + | |- | ||
| + | | valign="top"| | ||
| + | [[File:J22_radiation_hardness.png|thumb|left|340px| 07/29/2016]] | ||
| + | |} | ||
| + | |||
|} | |} | ||
Revision as of 16:42, 8 August 2016
| ⇐ Back to Crystal LOG |
| ⇐ Back to Neutral Particle Spectrometer |
| ⇐ Back to the Main_Page |
Time LOG
| Date | Description | Comments |
|---|---|---|
| 12/14/2015 | Pictures | Documentation of crystal's conditions as it arrived at CUA. |
| 01/28/2016 | Thermal annealing | Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. |
| 02/29/2016 | Light Yield | Run 3146: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. LY = 14.495 pe/MeV. |
| 03/04/2016 | Transverse Transmittance | At the center of the crystal, every nm from 200nm until 800nm. Sample: 1311 |
| 03/04/2016 | Dimensions | Crystal's dimensions measured. Length and six points of width (3 in each face). |
| 05/23/2016 | Transverse Transmittance Scan | Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/11/2016 | Longitudinal Transmittance Scan | Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/18/2016 | Transverse Transmittance Scan | Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/21/2016 | Xray Radiation | 70 minutes, 160mV, 6mA. 8th Shelf, 14.16cm LabJack height. |
| 07/21/2016 | Transverse Transmittance Scan | Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. |
Pictures at 12/14/2015
Radiation Hardness |