| Line 46: | Line 46: | ||
|07/25/16 || Transverse Transmittance || Wavelengths 200-800nm. | |07/25/16 || Transverse Transmittance || Wavelengths 200-800nm. | ||
|- | |- | ||
| − | |07/25/16 || LED curing || 7 minutes at 3.5 V with 34 blue LEDs. | + | |07/25/16 || LED curing || 7 more minutes (14 total) at 3.5 V with 34 blue LEDs. |
|- | |- | ||
|07/25/16 || Transverse Transmittance || Wavelengths 200-800nm. | |07/25/16 || Transverse Transmittance || Wavelengths 200-800nm. | ||
| + | |- | ||
| + | |08/08/2016 || Transverse Transmittance || Wavelengths 200-800nm. 10cm down crystal. Want to see if crystal recovers after 9 days of sitting in its casing. | ||
|} | |} | ||
Revision as of 16:45, 8 August 2016
| ⇐ Back to Crystal LOG |
| ⇐ Back to Neutral Particle Spectrometer |
| ⇐ Back to the Main_Page |
Time LOG
| Date | Description | Comments |
|---|---|---|
| 12/14/2015 | Pictures | Documentation of crystal's conditions as it arrived at CUA. |
| 01/28/2016 | Thermal annealing | Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. |
| 03/01/2016 | Light Yield | Run 3147: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. LY = 16.50 pe/MeV. |
| 03/04/2016 | Transverse Transmittance | At the center of the crystal, every nm from 200nm until 800nm. Sample: 1310 |
| 03/04/2016 | Dimensions | Crystal's dimensions measured. Length and six points of width (3 in each face). |
| 05/23/2016 | Transverse Transmittance Scan | Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/06/2016 | Longitudinal Transmittance Scan | Wavelengths: 200-800nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/18/2016 | Transverse Transmittance Scan | Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/18/2016 | X-ray Radiation | 70 minutes. 160kV. 6mA. 70 minutes ? cm from beam origin. |
| 07/18/2016 | Transverse Transmittance Scan | Wavelengths: 200-800nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/25/15 | X-ray Irradiation | 160kV 6.3mA 70 minutes. 14.16 cm for LabJack on shelf 8. 6290R/min ionization rate. |
| 07/25/16 | Transverse Transmittance | Wavelengths 200-800nm. |
| 07/25/16 | LED curing | 7 minutes at 3.5 V with 34 blue LEDs. |
| 07/25/16 | Transverse Transmittance | Wavelengths 200-800nm. |
| 07/25/16 | LED curing | 7 more minutes (14 total) at 3.5 V with 34 blue LEDs. |
| 07/25/16 | Transverse Transmittance | Wavelengths 200-800nm. |
| 08/08/2016 | Transverse Transmittance | Wavelengths 200-800nm. 10cm down crystal. Want to see if crystal recovers after 9 days of sitting in its casing. |