Difference between revisions of "MainPage:Nuclear:NPS:PWO:CrystalLOG:SICCAJ24"

Revision as of 16:55, 8 August 2016

⇐ Back to Crystal LOG

⇐ Back to Neutral Particle Spectrometer

⇐ Back to the Main_Page

**SICCA J24**
Date	Description	Comments
12/14/2015	Pictures	Documentation of crystal's conditions as it arrived at CUA.
01/28/2016	Thermal annealing	Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour.
03/02/2016	Light Yield	Run 3148: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. LY = 19.61 pe/MeV.
03/04/2016	Transverse Transmittance	At the center of the crystal, every nm from 200nm until 800nm. Sample: 1309
03/04/2016	Dimensions	Crystal's dimensions measured. Length and six points of width (3 in each face).
05/23/2016	Transverse Transmittance Scan	Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s.
07/11/2016	Longitudinal Transmittance Scan	Wavelengths: 200-800nm. Sampling period: 0.6s, moving motor at 2mm/s.
07/26/2016	Xray Radiation	70 minutes, 160mV, 6mA. ___ mm from beam origin.
07/26/2016	Transverse Transmittance Scan	Wavelengths: 200-800 nm. 10cm down.
07/26/2016	LED curing	34 LEDs, 3.5 V for 7 minutes.
07/26/2016	Transverse Transmittance Scan	Wavelengths: 200-800 nm. 10cm down.
08/01/2016	Transverse Transmittance Scan	Wavelengths: 200-800 nm. 10cm down. Crystal was most likely cured and preIR trans baseline was determined (wasn't done originally).