**SICCA J25**
Date	Description	Comments
12/14/2015	Pictures	Documentation of crystal's conditions as it arrived at CUA.
01/28/2016	Thermal annealing	Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour.
03/03/2016	Light Yield	Run 3149: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. LY = 13.07 pe/MeV.
03/04/2016	Transverse Transmittance	At the center of the crystal, every nm from 200nm until 800nm. Sample: 1308
03/04/2016	Dimensions	Crystal's dimensions measured. Length and six points of width (3 in each face).
05/23/2016	Transverse Transmittance Scan	Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s.
07/06/2016	Longitudinal Transmittance Scan	Wavelengths: 200-800nm.
07/18/2016	Transverse Transmittance Scan	Wavelengths: 200-800nm.
07/21/2016	Xray Radiation	70 minutes, 160mV, 6mA. ? mm from beam origin.
07/21/2016	Transverse Transmittance Scan	Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s.
07/27/16	X-Ray Radiation	160mV, 6.3 mA, 99 minutes.
07/27/16	Transverse Transmission	Wavelengths: 200-800nm.
07/27/2016	LED curing	34 LED's at 3.5 V for 7 minutes.
07/27/2016	Transverse Transmittance	Wavelengths: 200-800nm.

xxxx.

07/26/2016

07/26/2016

@@ Line 55: / Line 55: @@
 | valign="top"|
 [[File:SICCAJ25.JPG|thumb|center|340px|xxxx.]]
+|}
+==Radiation Hardness==
+{|border="0" style="text-align:center;" width="100%"
+|-
+| valign="top"|
+[[File:J25_radiation_hardness_redo.png|thumb|left|340px| 07/26/2016]]
+|}
+==LED curing==
+{|border="0" style="text-align:center;" width="100%"
+|-
+| valign="top"|
+[[File:J25_LED_curing.png|thumb|left|340px| 07/26/2016]]
 |}