Difference between revisions of "MainPage:Nuclear:NPS:PWO:CrystalLOG:SICCAJ28"
Jump to navigation
Jump to search
| Line 54: | Line 54: | ||
| valign="top"| | | valign="top"| | ||
[[File:SICCAJ28.JPG|thumb|center|340px|Cracks shown on edge of crystal.]] | [[File:SICCAJ28.JPG|thumb|center|340px|Cracks shown on edge of crystal.]] | ||
| + | |} | ||
| + | |||
| + | == Light Yield == | ||
| + | {|border="0" style="text-align:center;" width="100%" | ||
| + | |- | ||
| + | | valign="top"| | ||
| + | [[File:J28-100nsgw.png|thumb|left|340px| 07/26/2016]] | ||
| + | |} | ||
| + | |||
| + | ==Radiation Hardness== | ||
| + | {|border="0" style="text-align:center;" width="100%" | ||
| + | |- | ||
| + | | valign="top"| | ||
| + | [[File:J28_radiation_hardness.png|thumb|left|340px| 07/29/2016]] | ||
| + | |} | ||
| + | |||
| + | ==LED curing== | ||
| + | {|border="0" style="text-align:center;" width="100%" | ||
| + | |- | ||
| + | | valign="top"| | ||
| + | [[File:J28_LED_curing.png|thumb|left|340px| 07/29/2016]] | ||
|} | |} | ||
Revision as of 11:28, 9 August 2016
| ⇐ Back to Crystal LOG |
| ⇐ Back to Neutral Particle Spectrometer |
| ⇐ Back to the Main_Page |
Time LOG
| Date | Description | Comments |
|---|---|---|
| 03/09/2016 | Pictures | Documentation of crystal's conditions as it arrived at CUA. |
| 03/09/2016 | Dimensions | Crystal's dimensions measured. Length and six points of width (3 in each face). |
| 03/18/2016 | Thermal annealing | Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. |
| 04/03/2016 | Light Yield | Run 3169: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. LY = 15.09 pe/MeV. |
| 05/19/2016 | Transverse Transmittance | At the center of the crystal, every nm from 200nm until 800nm. Sample: 1343 |
| 05/20/2016 | Transverse Transmittance Scan | Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/11/2016 | Longitudinal Transmittance Scan | Wavelengths: 200-800nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/21/2016 | Transverse Transmittance | At 10cm. 200-800nm wavelength. |
| 07/23/2016 | Light Yield | Run:3239 ~3layers of teflon tape and 1 layer of black tape. ~50,000 incidents recorded at ~18 degrees Celsius. |
| 07/29/16 | X-Ray Irradiation | 160kV 6.3mA 70 minutes. 14.16 cm for LabJack on shelf 8. 6290R/min ionization rate. |
| 07/29/2016 | Transverse Transmittance | At 10cm. 200-800nm wavelength. |
| 07/29/2016 | LED curing | 7 minutes with 34 blue LEDs. 3.5 V. Millipore cover placed over lights and crystal. |
| 07/29/2016 | Transverse Transmittance | At 10cm. 200-800nm wavelength. |