Difference between revisions of "MainPage:Nuclear:NPS:PWO:CrystalLOG:SICCAJ24"
Jump to navigation
Jump to search
| Line 42: | Line 42: | ||
|- | |- | ||
| 08/01/2016 || Summer Students || Transverse Transmittance Scan || Wavelengths: 200-800 nm. 10cm down. Crystal was most likely cured and preIR trans baseline was determined (wasn't done originally). | | 08/01/2016 || Summer Students || Transverse Transmittance Scan || Wavelengths: 200-800 nm. 10cm down. Crystal was most likely cured and preIR trans baseline was determined (wasn't done originally). | ||
| + | |- | ||
| + | | 01/04/2017 || TH || Light Yield || Re-analyzed run 3148 with the same script and same limits as used for all runs taken in December 2016, LY = 18.9 pe/MeV'''. | ||
|} | |} | ||
Revision as of 12:52, 4 January 2017
| ⇐ Back to Crystal LOG |
| ⇐ Back to Neutral Particle Spectrometer |
| ⇐ Back to the Main_Page |
Time LOG
| Date | Experimenter(s) | Description | Comments |
|---|---|---|---|
| 12/14/2015 | Marco | Pictures | Documentation of crystal's conditions as it arrived at CUA. |
| 01/28/2016 | Marco | Thermal annealing | Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. |
| 03/02/2016 | Marco | Light Yield | Run 3148: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. LY = 19.61 pe/MeV. |
| 03/04/2016 | Marco | Transverse Transmittance | At the center of the crystal, every nm from 200nm until 800nm. Sample: 1309 |
| 03/04/2016 | Marco | Dimensions | Crystal's dimensions measured. Length and six points of width (3 in each face). |
| 05/23/2016 | Marco | Transverse Transmittance Scan | Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/11/2016 | Summer Students | Longitudinal Transmittance Scan | Wavelengths: 200-800nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/26/2016 | Summer Students | Xray Radiation | 70 minutes, 160mV, 6mA. ___ mm from beam origin. |
| 07/26/2016 | Summer Students | Transverse Transmittance Scan | Wavelengths: 200-800 nm. 10cm down. |
| 07/26/2016 | Summer Students | LED curing | 34 LEDs, 3.5 V for 7 minutes. |
| 07/26/2016 | Summer Students | Transverse Transmittance Scan | Wavelengths: 200-800 nm. 10cm down. |
| 08/01/2016 | Summer Students | Transverse Transmittance Scan | Wavelengths: 200-800 nm. 10cm down. Crystal was most likely cured and preIR trans baseline was determined (wasn't done originally). |
| 01/04/2017 | TH | Light Yield | Re-analyzed run 3148 with the same script and same limits as used for all runs taken in December 2016, LY = 18.9 pe/MeV. |