Difference between revisions of "MainPage:Nuclear:NPS:PWO:CrystalLOG:SICCAJ41"

Revision as of 11:43, 11 July 2017

⇐ Back to Crystal LOG

⇐ Back to Neutral Particle Spectrometer

⇐ Back to the Main_Page

**SICCA J41**
Date	Description	Comments
04/29/2016	Pictures	Documentation of crystal's conditions as it arrived at CUA.
04/29/2016	Thermal annealing	Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour.
05/19/2016	Transverse Transmittance	At the center of the crystal, every nm from 200nm until 800nm. Sample: 1355
05/20/2016	Light Yield	Run 3216: crystal wrapped with ~5 layers of teflon tape and 2 layers of black electrical tape. Steps of 20min, 1cm. T=18°C. LY = 12.53 ± 0.672 pe/MeV.
05/20/2016	Transverse Transmittance Scan	Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s.
07/08/2016	Longitudinal Transmittance Scan	Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s.
07/26/2016	Light Yield	Run: 3255. 3 layers of teflon tape, 1 layer of electrical tape. ~50,000 incidents. Light Yield: 13.40011277 pe/MeV
07/27/16	Light Yield	3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. 200ns gatewidth->900ns gatewidth. 200ns: 3321, 300ns:3322, 400ns:3323, 500ns:3324, 600ns:3325, 700ns:3328, 800ns:3329, 900ns:3330
07/07/2017	Longitudinal Transmittance Scan	Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s.
07/10/2017	Light Yield	Run 3694. 100ns gw. ~50,000 incidents ~3 layers of teflon tape ~1 layer of electrical. LY=7.509 pe/MeV.

xxxx.

07/26/2016

07/27/2016

@@ Line 38: / Line 38: @@
 | 07/07/2017 || Longitudinal Transmittance Scan || Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s.
 |-
-| 07/11/2017 || Light Yield || Run 3694. 100ns gw. ~50,000 incidents ~3 layers of teflon tape ~1 layer of electrical. LY=7.509 pe/MeV.
+| 07/10/2017 || Light Yield || Run 3694. 100ns gw. ~50,000 incidents ~3 layers of teflon tape ~1 layer of electrical. LY=7.509 pe/MeV.
 |}