Difference between revisions of "MainPage:Nuclear:NPS:PWO:CrystalLOG:SICCAJ36"
Jump to navigation
Jump to search
| (5 intermediate revisions by 3 users not shown) | |||
| Line 15: | Line 15: | ||
! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:10%;" | Date | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:10%;" | Date | ||
| + | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:15%;" | Experimenter(s) | ||
! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:15%;" | Description | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:15%;" | Description | ||
! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:75%;" | Comments | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:75%;" | Comments | ||
|- | |- | ||
| − | | 05/02/2016 || Pictures || Documentation of crystal's conditions as it arrived at CUA. | + | | 05/02/2016 || Marco || Pictures || Documentation of crystal's conditions as it arrived at CUA. |
|- | |- | ||
| − | | 05/02/2016 || Thermal annealing || Ramp up at 18°C/hour up to 200°C. Stays for 10 hours and ramp down at 18°C/hour. | + | | 05/02/2016 || Marco || Thermal annealing || Ramp up at 18°C/hour up to 200°C. Stays for 10 hours and ramp down at 18°C/hour. |
|- | |- | ||
| − | | 05/12/2016 || Light Yield || Run 3207: crystal wrapped with ~5 layers of teflon tape and 2 layers of black electrical tape. Steps of 20min, 1cm. T=18°C. LY = 21.137 ± 0.793 pe/MeV. | + | | 05/12/2016 || Salina || Light Yield || Run 3207: crystal wrapped with ~5 layers of teflon tape and 2 layers of black electrical tape. Steps of 20min, 1cm. T=18°C. LY = 21.137 ± 0.793 pe/MeV. |
|- | |- | ||
| − | | 05/19/2016 || Transverse Transmittance || At the center of the crystal, every nm from 200nm until 800nm. Sample: 1361 | + | | 05/19/2016 || Marco || Transverse Transmittance || At the center of the crystal, every nm from 200nm until 800nm. Sample: 1361 |
|- | |- | ||
| − | | 05/20/2016 || Transverse Transmittance Scan || Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. | + | | 05/20/2016 || Marco || Transverse Transmittance Scan || Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
|- | |- | ||
| − | | 07/07/2016 || Longitudinal Transmittance Scan || Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. | + | | 07/07/2016 || Marco || Longitudinal Transmittance Scan || Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. |
|- | |- | ||
| − | |07/25/16 || Light Yield || Run: 3251. 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. | + | |07/25/16 || Summer Students || Light Yield || Run: 3251. 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. Light Yield: 11.77 pe/MeV |
|- | |- | ||
| − | |07/27/16 || Light Yield || | + | |07/27/16 || Summer Students || Light Yield || 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. 200ns gatewidth->1000ns gatewidth. |
| − | + | 200ns: 3278, 300ns:3274, 400ns:3275, 500ns:3276, 600ns:3279, 700ns:3280, 800ns:3281,900ns:3282, 1000ns:3283 | |
| + | |- | ||
| + | |08/12/16 || Summer Students || Light Yield || Run: . 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. Light Yield: 11.77 pe/MeV | ||
| + | |- | ||
| + | |01/6/17 || Marco/TH || Irradiation X-ray || 160 kV, 6 mA, 15 min (+30 min), 160 kV, 6.2mA, 30 min | ||
|} | |} | ||
| Line 51: | Line 56: | ||
| valign="top"| | | valign="top"| | ||
[[File:J36-100nsgw.png|thumb|left|340px| 07/25/2016]] | [[File:J36-100nsgw.png|thumb|left|340px| 07/25/2016]] | ||
| + | | valign="top"| | ||
| + | [[File:J36-100nsgwREDO.png|thumb|left|340px| 07/25/2016]] | ||
|} | |} | ||
Latest revision as of 11:42, 20 September 2017
| ⇐ Back to Crystal LOG |
| ⇐ Back to Neutral Particle Spectrometer |
| ⇐ Back to the Main_Page |
Time LOG
| Date | Experimenter(s) | Description | Comments |
|---|---|---|---|
| 05/02/2016 | Marco | Pictures | Documentation of crystal's conditions as it arrived at CUA. |
| 05/02/2016 | Marco | Thermal annealing | Ramp up at 18°C/hour up to 200°C. Stays for 10 hours and ramp down at 18°C/hour. |
| 05/12/2016 | Salina | Light Yield | Run 3207: crystal wrapped with ~5 layers of teflon tape and 2 layers of black electrical tape. Steps of 20min, 1cm. T=18°C. LY = 21.137 ± 0.793 pe/MeV. |
| 05/19/2016 | Marco | Transverse Transmittance | At the center of the crystal, every nm from 200nm until 800nm. Sample: 1361 |
| 05/20/2016 | Marco | Transverse Transmittance Scan | Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/07/2016 | Marco | Longitudinal Transmittance Scan | Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/25/16 | Summer Students | Light Yield | Run: 3251. 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. Light Yield: 11.77 pe/MeV |
| 07/27/16 | Summer Students | Light Yield | 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. 200ns gatewidth->1000ns gatewidth.
200ns: 3278, 300ns:3274, 400ns:3275, 500ns:3276, 600ns:3279, 700ns:3280, 800ns:3281,900ns:3282, 1000ns:3283 |
| 08/12/16 | Summer Students | Light Yield | Run: . 3 layers of teflon 1 later of electrical. ~50,000 incidents at ~18 degrees Celsius. Light Yield: 11.77 pe/MeV |
| 01/6/17 | Marco/TH | Irradiation X-ray | 160 kV, 6 mA, 15 min (+30 min), 160 kV, 6.2mA, 30 min |
Pictures at 04/29/2016
Light Yield
|
File:J36-100nsgwREDO.png 07/25/2016 |