Difference between revisions of "MainPage:Nuclear:NPS:PWO:CrystalLOG:SICCAJ40"
Jump to navigation
Jump to search
| (3 intermediate revisions by 2 users not shown) | |||
| Line 15: | Line 15: | ||
! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:10%;" | Date | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:10%;" | Date | ||
| + | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:15%;" | Experimenter(s) | ||
! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:15%;" | Description | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:15%;" | Description | ||
! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:75%;" | Comments | ! "background:#f5f5f5;" style="text-align:center; background:lavender; font-weight:bold; width:75%;" | Comments | ||
|- | |- | ||
| − | | 04/29/2016 || Pictures || Documentation of crystal's conditions as it arrived at CUA. | + | | 04/29/2016 || Salina || Pictures || Documentation of crystal's conditions as it arrived at CUA. |
|- | |- | ||
| − | | 04/29/2016 || Thermal annealing || Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. | + | | 04/29/2016 || Marco || Thermal annealing || Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. |
|- | |- | ||
| − | | 05/15/2016 || | + | | 05/15/2016 || Salina || Crystal Cracked || Crystal was slightly cracked toward the edges due to an accident. Some pieces of this crystal will be used to measure the chemical composition. |
|- | |- | ||
| − | | 05/19/2016 || Light Yield || Run | + | | 05/19/2016 || Salina || Light Yield || Run 3214: crystal wrapped with ~5 layers of teflon tape and 2 layers of black electrical tape. Steps of 20min, 1cm. T=18°C. LY = 14.7962 ± 0.575 pe/MeV. |
|- | |- | ||
| − | | 05/20/2016 || Transverse Transmittance|| At the center of the crystal, every nm from 200nm until 800nm. Sample: | + | | 05/20/2016 || Marco || Transverse Transmittance || At the center of the crystal, every nm from 200nm until 800nm. Sample: 1366 |
|- | |- | ||
| − | | 05/20/2016 || Transverse Transmittance Scan || Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. | + | | 05/20/2016 || Marco || Transverse Transmittance Scan || Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| + | |- | ||
| + | | 07/07/2016 || Marco || Longitudinal Transmittance Scan || Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. | ||
|} | |} | ||
Latest revision as of 11:55, 20 September 2017
| ⇐ Back to Crystal LOG |
| ⇐ Back to Neutral Particle Spectrometer |
| ⇐ Back to the Main_Page |
Time LOG
| Date | Experimenter(s) | Description | Comments |
|---|---|---|---|
| 04/29/2016 | Salina | Pictures | Documentation of crystal's conditions as it arrived at CUA. |
| 04/29/2016 | Marco | Thermal annealing | Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. |
| 05/15/2016 | Salina | Crystal Cracked | Crystal was slightly cracked toward the edges due to an accident. Some pieces of this crystal will be used to measure the chemical composition. |
| 05/19/2016 | Salina | Light Yield | Run 3214: crystal wrapped with ~5 layers of teflon tape and 2 layers of black electrical tape. Steps of 20min, 1cm. T=18°C. LY = 14.7962 ± 0.575 pe/MeV. |
| 05/20/2016 | Marco | Transverse Transmittance | At the center of the crystal, every nm from 200nm until 800nm. Sample: 1366 |
| 05/20/2016 | Marco | Transverse Transmittance Scan | Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/07/2016 | Marco | Longitudinal Transmittance Scan | Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. |