Difference between revisions of "MainPage:Nuclear:NPS:PWO:CrystalLOG:CRYTUR01"

Revision as of 15:05, 12 August 2016

⇐ Back to Crystal LOG

⇐ Back to Neutral Particle Spectrometer

⇐ Back to the Main_Page

**CRYTUR 01**
Date	Description	Comments
xx/xx/2015	Wrapped	Preparing for light yield measurement. Approximately 5 layers of teflon tape, and 2 layers of black tape.
xx/xx/2015	LY scan	...
12/14/2015	unwrapped	Preparing for annealing.
12/14/2015	Thermal annealing	Starting 11:00AM. Ramp up at 18oC/hour until 200oC, stay at 200oC for 10 hours, ramp down at -18oC/hour.
12/17/2015	Longitudinal Transmittance	After annealing.
07/15/2016	Longitudinal Transmittance	Wavelength:200-800nm.
08/11/2016	LY scan	RUN:3411. Motor was lowered to approximately 5 cm down crystal. ~18oC. LY: 11.986 phe/MeV

Longitudinal transmittance measured at Lambda 750 (no integrating sphere).

CRYTUR shown inside oven.

Graph showing CRYTUR crystal longitudinal measurements before annealing (red) and after annealing (green).

Graph showing the difference of the CRYTUR crystal longitudinal measurements before and after annealing.

@@ Line 29: / Line 29: @@
 |-
 | 07/15/2016 || Longitudinal Transmittance || Wavelength:200-800nm.
+|-
+| 08/11/2016 || LY scan || RUN:3411. Motor was lowered to approximately 5 cm down crystal. ~18oC. LY: 11.986 phe/MeV
 |}