MainPage:Nuclear:NPS:PWO:CrystalLOG:SICCAJ20

⇐ Back to Crystal LOG

⇐ Back to Neutral Particle Spectrometer

⇐ Back to the Main_Page

Time LOG

SICCA J20

Date	Experimenter(s)	Description	Comments
12/14/2015	Marco	Pictures	Documentation of crystal's conditions as it arrived at CUA.
12/15/2015	Marco	Thermal annealing	Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour.
12/17/2015	Marco	Transverse Transmittance	Scan at 360, 420, and 620nm.
12/18/2015	Marco	Irradiation	160 keV photons at 6mA, for 10min.
12/18/2015	Marco	Transverse Transmittance	Scan at 360, 420, and 620nm after 30 min of irradiation.
01/07/2016	Marco	LY scan	LY measurement with window width of 100ns, at 18oC (see run 3098). LY = 14.76 pe/MeV.
03/04/2016	Marco	Transverse Transmittance	At the center of the crystal, every nm from 200nm until 800nm. Sample: 1313
03/04/2016	Marco and Salina	Dimensions	Crystal's dimensions measured. Length and six points of width (3 in each face).
05/23/2016	Marco	Transverse Transmittance Scan	Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s.
07/08/2016	Marco	Longitudinal Transmittance Scan	Wavelengths: 200-800 nm. Measured effect of off-center placement of crystal on transmittance. +1.3°, +2.3°, -1.3°, -2.3.
07/08/2016	Summer Students	Longitudinal Transmittance Scan	Wavelengths: 200-800 nm. Measured light beam entering both end face of crystal in spectrometer. "flip" of crystal.
07/23/2016	Summer Students	Light Yield	Run: 3246. 3 layers of teflon tape and 1 of electrical. ~50.000 incidents and ~18 degrees Celsius
07/28/2016	Summer Students	Transverse Transmittance	At 10cm. 200-800nm wavelength.
07/28/2016	Summer Students	X-Ray Irradiation	160kV 6.3mA 70 minutes. 14.16 cm for LabJack on shelf 8. 6290R/min ionization rate.
07/28/2016	Summer Students	Transverse Transmittance (spectrometer failure)	Unsuccessful measurement of transmittance.
07/07/2017	Summer Students	Transverse Transmittance	200-800nm wavelengths. Sampling period: 0.6s, moving motor at 2mm/s.
07/07/2017	Summer Students	Irradiation	160 keV photons at 6.3mA, for 90min. (Unsuccessful due to fuse shorting)
07/27/2017	Summer Students	Transverse Transmittance Scan	Wavelengths: 200-800 nm. 10cm down.
07/27/2017	Summer Students	Xray Radiation	70 minutes, 160mV, 6mA. ___ mm from beam origin.
07/27/2017	Summer Students	Transverse Transmittance Scan	Wavelengths: 200-800 nm. 10cm down.
07/27/2017	Summer Students	LED curing	34 LEDs, 3.5 V for 7 minutes.
07/27/2017	Summer Students	Transverse Transmittance Scan	Wavelengths: 200-800 nm. 10cm down.
07/27/2017	Summer Students	LED curing	34 LEDs, 3.5 V for 7 minutes.
07/27/2017	Summer Students	Transverse Transmittance Scan	Wavelengths: 200-800 nm. 10cm down.
07/27/2017	Summer Students	LED curing	34 LEDs, 3.5 V for 7 minutes.
07/27/2017	Summer Students	Transverse Transmittance Scan	Wavelengths: 200-800 nm. 10cm down.

Pictures at 12/14/2015

xxxx.

xxxx.

Light Yield

07/23/2016

Irradiation Studies

07/27/2017

LED Curing

07/27/2017