| Line 65: | Line 65: | ||
[[File:SICCAJ30.JPG|thumb|center|340px|Stain shown on surface of crystal on one end.]] | [[File:SICCAJ30.JPG|thumb|center|340px|Stain shown on surface of crystal on one end.]] | ||
|} | |} | ||
| − | == | + | == Irradiation Studies == |
{|border="0" style="text-align:center;" width="100%" | {|border="0" style="text-align:center;" width="100%" | ||
|- | |- | ||
| valign="top"| | | valign="top"| | ||
| − | [[File: | + | [[File:J30IR.png|thumb|left|340px| 07/27/2016 ]] |
| + | |} | ||
| + | |||
| + | == LED Curing== | ||
| + | {|border="0" style="text-align:center;" width="100%" | ||
| + | |- | ||
| valign="top"| | | valign="top"| | ||
| − | [[File: | + | [[File:J30LED.png|thumb|left|340px| 07/27/2016 ]] |
| − | |||
|} | |} | ||
Latest revision as of 11:33, 2 August 2017
| ⇐ Back to Crystal LOG |
| ⇐ Back to Neutral Particle Spectrometer |
| ⇐ Back to the Main_Page |
Time LOG
| Date | Experimenter(s) | Description | Comments |
|---|---|---|---|
| 03/09/2016 | Salina | Pictures | Documentation of crystal's conditions as it arrived at CUA. |
| 03/09/2016 | Salina and Marco | Dimensions | Crystal's dimensions measured. Length and six points of width (3 in each face). |
| 03/18/2016 | Marco | Thermal annealing | Ramp up at 18oC/hour up to 200oC. Stays for 10 hours and ramp down at 18oC/hour. |
| 04/13/2016 | Salina | Light Yield | Run 3171: crystal wrapped with ~5 layers of teflon tape and 2 layers of black tape. Steps of 20min, 1cm. T=18oC. LY = 14.95 pe/MeV. |
| 05/17/2016 | Salina | Transverse Transmittance | At the center of the crystal, every nm from 200nm until 800nm. Sample: 1341 |
| 05/20/2016 | Marco | Transverse Transmittance Scan | Wavelengths: 360nm, 420nm, 620nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/06/2016 | Summer Students | Longitudinal Transmittance Scan | Wavelengths: 200-800 nm. Sampling period: 0.6s, moving motor at 2mm/s. |
| 07/23/2016 | Summer Students | Light Yield | Run:3236 ~3layers of teflon tape and 1 layer of black tape. ~50,000 incidents recorded at ~18 degrees Celsius. |
| 08/01/2016 | Summer Students | Transverse Transmittance Scan | All wavelenghts, 10cm down the crystal. |
| 08/11/2016 | Summer Students | Light Yield | Run:3409 ~3layers of teflon tape and 1 layer of black tape. ~50,000 incidents recorded at ~18 degrees Celsius. LY: 12.18pe/MeV |
| 07/27/2017 | Summer Students | Transverse Transmittance Scan | Wavelengths: 200-800 nm. 10cm down. |
| 07/27/2017 | Summer Students | Xray Radiation | 70 minutes, 160mV, 6mA. ___ mm from beam origin. |
| 07/27/2017 | Summer Students | Transverse Transmittance Scan | Wavelengths: 200-800 nm. 10cm down. |
| 07/27/2017 | Summer Students | LED curing | 34 LEDs, 3.5 V for 7 minutes. |
| 07/27/2017 | Summer Students | Transverse Transmittance Scan | Wavelengths: 200-800 nm. 10cm down. |
| 07/27/2017 | Summer Students | LED curing | 34 LEDs, 3.5 V for 7 minutes. |
| 07/27/2017 | Summer Students | Transverse Transmittance Scan | Wavelengths: 200-800 nm. 10cm down. |
| 07/27/2017 | Summer Students | LED curing | 34 LEDs, 3.5 V for 7 minutes. |
| 07/27/2017 | Summer Students | Transverse Transmittance Scan | Wavelengths: 200-800 nm. 10cm down. |